Geomembranes are made from impermeable geosynthetic material consisting of thin continuous sheets of polymers. Geomembranes create an impermeable barrier that prevents the leakage of harmful contaminants or dangerous chemicals to surrounding environments. It is also regularly used as containment barriers for potable water and irrigation storage requirements to prevent leakage. Geomembranes are used in conjunction with other geosynthetic products to control fluid movement and provide containment in projects related to mining, sewage treatment and canal construction.
The growing application of geomembranes is noticeable in different industries due to the versatility of the product. Geomembranes have a wide range of applications in industries such as mining, marine, civil, water treatment and transportation. Some of the applications are detailed below.
| Product Name: | ISO Certification 0.75mm GM 13 HDPE Geomembrane Shrimp Pond Liner |
| Thickness: | 0.2mm-3.0mm(Main:0.5mm, 0.75mm,1.0mm,1.5mm,2.0mm) |
| Length : | 50m/roll,100m/roll,150m/roll or follow your request |
| width: | 1m-8m or follow customers' demand, Main width is 4m,5m,5.8m,6.0m |
| Surface | Both side smooth/both side textured one side textured one side smooth, or as your request |
| Color: | White,Black,Green,Blue,mainly black |
| Material: | HDPE,LDPE,LLDPE, ( 100% Virgin) |
| Certification: | ISO9001:2008,CE |
| Standard: | ASTM GRI-GM13 |
Usage of geomembrane in the mining industry started in the 1970s and has increased thereafter. It is used as a lining solution for evaporation ponds, heap leach pads and tailing impoundments.
The design and construction of these heap leach pads are regulated to protect the environment from exposure to harmful chemicals so a lining system, usually a HDPE geomembrane, forms a critical component in construction of these heap leach facilities.
Geomembranes are also used during the end of a mine's lifespan. As a part of mine restoration, HDPE liners are used to seal the mine and prevent waste products from contaminating the surrounding environment. Overall, geomembrane lining is a safe and effective solution to protect the environment from harmful industries.
Water Industry
HDPE geomembranes play a major role in delivering clean water to the community. They are used in services related to drinking water and wastewater including sewage treatment. When canals, dams and reservoirs are sealed with geomembrane liners they avoid contamination from groundwater.
Geomembrane is also used to prevent contamination of potable water from soil and other pollutants as well as preventing loss of water through infiltration of the water into the surrounding soil. Lining a dam or canal can minimise seepage thereby improving the efficiency of storage and transportation. Geomembranes are also used as a secondary containment for underground storage tanks, solar ponds and brine solution.
More application
Index
| S/N |
Item | Index | ||||||
| Thickness mm | 0.75 | 1.00 | 1.25 | 1.50 | 2.00 | 2.50 | 3.00 | |
| 1 | Density g/cm3 | ≥0.940 | ||||||
| 2 | Tensile yield strength (vertical and horizontal) N/mm | ≥11 | ≥15 | ≥18 | ≥22 | ≥29 | ≥37 | ≥44 |
| 3 | Tensile breaking strength (vertical and horizontal) N/mm | ≥20 | ≥27 | ≥33 | ≥40 | ≥53 | ≥67 | ≥80 |
| 4 | Elongation (vertical and horizontal) % | - | - | - | ≥12 | |||
| 5 | Elongation at break (vertical and horizontal) % | ≥700 | ||||||
| 6 | Tearing load at right angle (vertical and horizontal) N | ≥93 | ≥125 | ≥160 | ≥190 | ≥250 | ≥315 | ≥375 |
| 7 | Anti-puncture strength N | ≥240 | ≥320 | ≥400 | ≥480 | ≥540 | ≥800 | ≥960 |
| 8 | Tensile load stress cracking (tensile method of dead load of the cut) h | _ | ≥300 | |||||
| 9 | Carbon black content % | 2.0~3.0 | ||||||
| 10 | Carbon black dispersion | The number of Level 3 among 10 data is not more than one; Level 4 and Level 5 are not allowed. | ||||||
| Oxidation induction time (OIT) min | Oxidation induction time under normal pressure ≥100 | |||||||
| 11 | Oxidation induction time under disjoining pressure ≥400 | |||||||
| 12 | 85°C thermal aging (retention rate of OIT under normal pressure after 90d) % | ≥55 | ||||||
| 13a | Ultraviolet resistance (retention rate of OIT after 1600h ultraviolet irradiation) % | ≥50 | ||||||
| Note: Technical performance index of thickness specification not listed in the table shall be implemented according to interpolation method. | ||||||||
| For two indexes of Item 11 and Item 13, select one from retention rate of OIT under normal pressure and retention rate of OIT under high pressure and carry out the test. | ||||||||